This paper describes a laboratory study of causes of external casing corrosion and the test work that led to the use of oxygen scavengers to prevent this attack. External casing failures are classified as water-line, casing-casing, collar and body failures. A corrosion mechanism based on principles of differential oxygen availability is developed that is consistent with facts known about each kind of failure. The field use of oxygen scavengers is depicted as a direct result of the laboratory study.
A part of the paper is devoted to reporting on the field use of hydrazine to control external casing corrosion. Results of field measurements made over a period of several years are presented as evidence of the effectiveness of the hydrazine treatment. The first conclusion reached is that the use of hydrazine materially reduces the cathodic protection requirements for treated wells. This result is interpreted to mean that a reduction is taking place in the amount of corrosion on the casing. Results indicate also that hydrazine shows its greatest usefulness within the first 12 to 18 months after a well is completed when pitting corrosion is likely to be most active.